耐油性 PA66 A3HG5 德國巴斯夫 尺寸穩(wěn)定 加纖25% 機(jī)械部件 外殼 Ultramid? A3HG5Polyamide 66BASF Corporation25% 玻璃纖維增強(qiáng)材料產(chǎn)品說明：Ultramid A3HG5 is a 25% glass fiber reinforced injection molding PA66 grade.ApplicationsTypical applications include machinery components and housings of high stiffness and dimensional stability.物性信息：基本信息黃卡編號(hào)E36632-531624E41871-233734填料/增強(qiáng)材料玻璃纖維增強(qiáng)材料, 25% 填料按重量特性尺寸穩(wěn)定性良好剛性，高耐油性能用途機(jī)器/機(jī)械部件外殼機(jī)構(gòu)評(píng)級(jí)EC 1907/2006 (REACH)RoHS 合規(guī)性RoHS 合規(guī)形式粒子加工方法注射成型多點(diǎn)數(shù)據(jù)Creep Modulus vs. Time (ISO 11403-1)Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)物理性能干燥調(diào)節(jié)后的單位制測(cè)試方法比重1.32--g/cm3ASTM D792, ISO 1183溶化體積流率（MVR） (275°C/5.0 kg)50.0--cm3/10minISO 1133收縮率 - 流動(dòng) (3.18 mm)0.30--%吸水率     飽和6.0--%ASTM D570     飽和, 23°C6.0--%ISO 62     平衡, 50% RH1.9--%ASTM D570     平衡, 23°C, 50% RH1.9--%ISO 62機(jī)械性能干燥調(diào)節(jié)后的單位制測(cè)試方法拉伸模量 (23°C)86006500MPaISO 527-2抗張強(qiáng)度     斷裂, 23°C179--MPaASTM D638     斷裂, -40°C196186MPaISO 527-2     斷裂, 23°C170120MPaISO 527-2伸長(zhǎng)率     斷裂, 23°C3.0--%ASTM D638     斷裂, 23°C3.06.0%ISO 527-2彎曲模量     23°C7930--MPaASTM D790     23°C7600--MPaISO 178沖擊性能干燥調(diào)節(jié)后的單位制測(cè)試方法簡(jiǎn)支梁缺口沖擊強(qiáng)度ISO 179     -30°C9.0--kJ/m2ISO 179     23°C1018kJ/m2ISO 179簡(jiǎn)支梁無缺口沖擊強(qiáng)度ISO 179     -30°C55--kJ/m2ISO 179     23°C6590kJ/m2ISO 179懸壁梁缺口沖擊強(qiáng)度     -40°C53--J/mASTM D256     23°C96--J/mASTM D256     23°C9.5--kJ/m2ISO 180熱性能干燥調(diào)節(jié)后的單位制測(cè)試方法載荷下熱變形溫度     0.45 MPa, 未退火250--°CASTM D648, ISO 75-2/B     1.8 MPa, 未退火250--°CASTM D648, ISO 75-2/A熔融峰值溫度260--°CASTM D3418, ISO 3146